Nickel Alloy 201 Rods Manufacturer, High Nickel Alloy 201 Flat Bars, UNS N02200 Threaded Bar/Rod, Nickel Alloy 201 Bars, Nickel Alloy 201 Forged Round Bars Exporter.
These are also referred as UNS N02201 Round Bars and WNR 2.4066 Round Bars. Nickel 201 Round Bars (Nickel Alloy 201 Bars) can be electroplated and are effortlessly welded, making them appropriate for use in industries where very much high and low temperatures come into drama. Nickel 201 Rods (Nickel Alloy 201 Rods) provides extremely ductile mechanical features all over an extensive temperature range. Meanwhile, we as well offer the same in customized thicknesses and sizes as per the precise requirements given by our valuable customers in international quality of standards.
These properties and its chemical composition make Nickel 201 fabricatable and highly resistant to corrosive environments. Nickel 201 is useful in any environment below 600º F. It is highly resistant to corrosion by neutral and alkaline salt solutions. Nickel alloy 201 also has low corrosion rates in neutral and distilled water. This nickel alloy can be hot formed to any shape and formed cold by all methods.
| STANDARD | WERKSTOFF NR. | UNS | JIS | AFNOR | BS | GOST | EN |
| Nickel Alloy 201 | 2.4068 | N02201 | NW 2201 | - | NA 12 | НП-2 | Ni 99.0 |
| Element | Content (%) |
|---|---|
| Nickel, Ni | ≥ 99 |
| Iron, Fe | ≤ 0.40 |
| Manganese, Mn | ≤ 0.35 |
| Silicon, Si | ≤ 0.35 |
| Copper, Cu | ≤ 0.25 |
| Carbon, C | ≤ 0.15 |
| Sulfur, S | ≤ 0.010 |
| Properties | Metric | Imperial |
|---|---|---|
| Density | 8.89 g/cm3 | 0.321 lb/in3 |
| Melting point | 1435-1446°C | 2615-2635°F |
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength (annealed) | 462 MPa | 67000 psi |
| Yield strength (annealed) | 148 MPa | 21500 psi |
| Elongation at break (annealed prior to test) | 45% | 45% |
| Properties | Metric | Imperial |
|---|---|---|
| Thermal expansion co-efficient (@20-100°C/68-212°F) | 13.3 µm/m°C | 7.39 µin/in°F |
| Thermal conductivity | 70.2 W/mK | 487 BTU.in/hrft².°F |
Nickel 201 alloy can be shaped through all hot working and cold working practices. The alloy can be hot worked between 649°C (1200°F) and 1232°C (2250°F), with heavy forming carried out at temperatures above 871°C (1600°F). Annealing is performed at temperature between 704°C (1300°F) and 871°C (1600°F).
Carey Alloys Nickel 201 alloy to countries like UAE, Bahrain, Italy, Indonesia, Malaysia, United States, Mexico, Chine, Brazil, Peru, Nigeria, Kuwait, Jordan, Dubai, Thailand (Bangkok), Venezuela, Iran, Germany, UK, Canada, Russia, Turkey, Australia, New Zealand, Sri Lanka, Vietnam, South Africa, Kazakhstan & Saudi Arabia.
HASTELLOY, HAYNES and C-22 are registered trade names of Haynes International, Inc., MONEL & INCONEL are registered trade names of INCO family of companies., NITRONIC is a registered trade name of Armco Inc., CARPENTER & 20Cb-3 are registered trade names of Carpenter Technology Corporation., FERRALIUM is a registered trade name of Langley Alloys, LTD.