As a much-admired organization in the market, we as Carey Alloys are quite engaged in proposing a collection of Nickel Alloy 201 Flanges as an exporter, manufacturer, supplier, and stockiest to our worldwide clients at reasonably priced costs.
Nickel Alloy Plate Flanges, High Nickel 200 Blind Flanges, Nickel Alloy 201 Slip On Flanges, Nickel N02201 Industrial Flanges Exporter.
With respect to different grades, we offer these flanges in different types such as Nickel Alloy 201 Slip On Flanges, Nickel Alloy 201 Blind Flanges, Nickel Alloy 200 Weld Neck Flanges, Nickel Alloy 201 Socket Weld Flanges, Nickel Alloy 200 Spectacle Blind Flanges, Nickel Alloy 201 Screwed / Threaded Flanges, Nickel Alloy 200 Reducing Flanges, and Nickel Alloy 201 Ring Type Joint Flanges (RTJ). Meanwhile, with respect to national and international quality of raw materials, we also offer these UNS N02200 Flanges / WNR 2.4066 Flanges and UNS N02201 Flanges / WNR 2.4068 Flanges in customized sizes and thicknesses as per specific demands by our esteemed clients at market leading prices.
These properties and its chemical composition make Nickel 200 fabricatable and highly resistant to corrosive environments. Nickel 200 is useful in any environment below 600º F. It is highly resistant to corrosion by neutral and alkaline salt solutions. Nickel alloy 200 also has low corrosion rates in neutral and distilled water. This nickel alloy can be hot formed to any shape and formed cold by all methods.
| STANDARD | WERKSTOFF NR. | UNS | JIS | AFNOR | BS | GOST | EN |
| Nickel Alloy 201 | 2.4068 | N02201 | NW 2201 | - | NA 12 | НП-2 | Ni 99 |
| Element | Content (%) |
|---|---|
| Nickel, Ni | ≥ 99 |
| Iron, Fe | ≤ 0.40 |
| Manganese, Mn | ≤ 0.35 |
| Silicon, Si | ≤ 0.35 |
| Copper, Cu | ≤ 0.25 |
| Carbon, C | ≤ 0.15 |
| Sulfur, S | ≤ 0.010 |
| Properties | Metric | Imperial |
|---|---|---|
| Density | 8.89 g/cm3 | 0.321 lb/in3 |
| Melting point | 1435-1446°C | 2615-2635°F |
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength (annealed) | 462 MPa | 67000 psi |
| Yield strength (annealed) | 148 MPa | 21500 psi |
| Elongation at break (annealed prior to test) | 45% | 45% |
| Properties | Metric | Imperial |
|---|---|---|
| Thermal expansion co-efficient (@20-100°C/68-212°F) | 13.3 µm/m°C | 7.39 µin/in°F |
| Thermal conductivity | 70.2 W/mK | 487 BTU.in/hrft².°F |
Nickel 201 alloy can be shaped through all hot working and cold working practices. The alloy can be hot worked between 649°C (1200°F) and 1232°C (2250°F), with heavy forming carried out at temperatures above 871°C (1600°F). Annealing is performed at temperature between 704°C (1300°F) and 871°C (1600°F).
Carey Alloys Nickel 201 alloy to countries like UAE, Bahrain, Italy, Indonesia, Malaysia, United States, Mexico, Chine, Brazil, Peru, Nigeria, Kuwait, Jordan, Dubai, Thailand (Bangkok), Venezuela, Iran, Germany, UK, Canada, Russia, Turkey, Australia, New Zealand, Sri Lanka, Vietnam, South Africa, Kazakhstan & Saudi Arabia.
HASTELLOY, HAYNES and C-22 are registered trade names of Haynes International, Inc., MONEL & INCONEL are registered trade names of INCO family of companies., NITRONIC is a registered trade name of Armco Inc., CARPENTER & 20Cb-3 are registered trade names of Carpenter Technology Corporation., FERRALIUM is a registered trade name of Langley Alloys, LTD.