It provides good resistance to carburization, oxidation, and nitridation. RA 330 is also easily welded using all conventional processes; it can be formed hot (between 1750-1200° F) and cold.
Alloy A286 sheet can be solution treated at the temperatures detailed below, rapid cooled and then age hardened at 1325ºF (720ºC) for 16 hours and air cooling. The 1800ºF (980ºC) solution treatment produces the highest creep-rupture strength in age-hardened material whereas the 1650ºF (900ºC) treatment results in improved ductility and room temperature strength.
|
Chemical Analysis |
|
|
C |
.08 max |
|
MN |
2.00 max |
|
P |
.03 max |
|
S |
.03 max |
|
Si |
.75- 1.50 |
|
Cr |
17.0- 20.0 |
|
Ni |
34.0- 37.0 |
|
Mo |
1.00- 1.75 |
|
Cu |
1.00 max |
|
Ti |
1.90- 2.30 |
|
Fe |
bal |
|
Sn |
.025 |
|
pb |
.005 max |
Carey Alloys export products to countries like UAE, Bahrain, Italy, Indonesia, Malaysia, United States, Mexico, Chine, Brazil, Peru, Nigeria, Kuwait, Jordan, Dubai, Thailand (Bangkok), Venezuela, Iran, Germany, UK, Canada, Russia, Turkey, Australia, New Zealand, Sri Lanka, Vietnam, South Africa, Kazakhstan & Saudi Arabia.
HASTELLOY, HAYNES and C-22 are registered trade names of Haynes International, Inc., MONEL & INCONEL are registered trade names of INCO family of companies., NITRONIC is a registered trade name of Armco Inc., CARPENTER & 20Cb-3 are registered trade names of Carpenter Technology Corporation., FERRALIUM is a registered trade name of Langley Alloys, LTD.