As an acclaimed enterprise of the industry, Carey Alloys is involved in offering a vast array of Nickel Alloy Butt Weld Pipe Fittings as a manufacturer, exporter, stockiest and supplier to our domestic and global clients
ANSI/ASME B16.9 Nickel Alloy Seamless Buttweld Pipe Fittings, MSS-SP-43 Nickel Alloy UNS N02201 Welded Butt weld Fitttings Exporter.
With respect to different grades, we offer these Nickel Alloy Pipe Fittings in different types such as Nickel Alloy 201 Seamless Butt weld pipe fittings, Nickel Alloy 201 Welded Butt weld pipe fittings, Nickel Alloy 200 Elbow (45deg, 90deg, 180deg), Nickel Alloy 201 Equal & Unequal (reducing) Tees, Nickel Alloy 200 Equal & Unequal (reducing) Cross, Nickel Alloy 201 Concentric & Eccentric Reducer, Nickel Alloy 201 Long & Short Stubends, and Nickel Alloy 200 Pipe End Caps. With respect to national and international quality of raw materials, we also offer these UNS N02200 Butt Weld Pipe Fittings / WNR 2.4066 Butt Weld Pipe Fittings and UNS N02201 Butt Weld Pipe Fittings / WNR 2.4068 Butt Weld Pipe Fittings in customized sizes and thicknesses as per specific demands by our esteemed clients at market leading prices.
These properties and its chemical composition make Nickel 201 fabricatable and highly resistant to corrosive environments. Nickel 200 is useful in any environment below 600º F. It is highly resistant to corrosion by neutral and alkaline salt solutions. Nickel alloy 200 also has low corrosion rates in neutral and distilled water. This nickel alloy can be hot formed to any shape and formed cold by all methods.
| STANDARD | WERKSTOFF NR. | UNS | JIS | AFNOR | BS | GOST | EN |
| Nickel Alloy 201 | 2.4068 | N02201 | NW 2201 | - | NA 12 | НП-2 | Ni 99 |
| Element | Content (%) |
|---|---|
| Nickel, Ni | ≥ 99 |
| Iron, Fe | ≤ 0.40 |
| Manganese, Mn | ≤ 0.35 |
| Silicon, Si | ≤ 0.35 |
| Copper, Cu | ≤ 0.25 |
| Carbon, C | ≤ 0.15 |
| Sulfur, S | ≤ 0.010 |
| Properties | Metric | Imperial |
|---|---|---|
| Density | 8.89 g/cm3 | 0.321 lb/in3 |
| Melting point | 1435-1446°C | 2615-2635°F |
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength (annealed) | 462 MPa | 67000 psi |
| Yield strength (annealed) | 148 MPa | 21500 psi |
| Elongation at break (annealed prior to test) | 45% | 45% |
| Properties | Metric | Imperial |
|---|---|---|
| Thermal expansion co-efficient (@20-100°C/68-212°F) | 13.3 µm/m°C | 7.39 µin/in°F |
| Thermal conductivity | 70.2 W/mK | 487 BTU.in/hrft².°F |
Nickel 201 alloy can be shaped through all hot working and cold working practices. The alloy can be hot worked between 649°C (1200°F) and 1232°C (2250°F), with heavy forming carried out at temperatures above 871°C (1600°F). Annealing is performed at temperature between 704°C (1300°F) and 871°C (1600°F).
Carey Alloys Nickel 201 alloy to countries like UAE, Bahrain, Italy, Indonesia, Malaysia, United States, Mexico, Chine, Brazil, Peru, Nigeria, Kuwait, Jordan, Dubai, Thailand (Bangkok), Venezuela, Iran, Germany, UK, Canada, Russia, Turkey, Australia, New Zealand, Sri Lanka, Vietnam, South Africa, Kazakhstan & Saudi Arabia.
HASTELLOY, HAYNES and C-22 are registered trade names of Haynes International, Inc., MONEL & INCONEL are registered trade names of INCO family of companies., NITRONIC is a registered trade name of Armco Inc., CARPENTER & 20Cb-3 are registered trade names of Carpenter Technology Corporation., FERRALIUM is a registered trade name of Langley Alloys, LTD.