Maraging steels sheet are supplied in the annealed condition where the microstructure consists of fine martensite. Aging to achieve final properties is a relatively low temperature procedure giving the required high strength and toughness. This low temperature treatment allows for machining close to final size since distortion is minimal. Maraging steels sheet also retain their strength up to 450◦C (840◦F), can be nitride and have a corrosion resistance similar to that of standard martensitic stainless steels.
Maraging C250 Sheet is the lowest strength of the maraging steels stocked by Carey Alloys . Typical usage is in jet engine shafts, missile casings, ordinance mounting blocks and tooling.
| Weight% | Ni | Co | Mn | Si | C | Al | Mo | S | P | Ti | Fe | Cr | Cu |
| C250 | 17.0 / 19.0 | 7.0 / 8.5 | 0.10 max | 0.10 max | 0.03 max | 0.05 / 0.15 | 4.6 / 5.2 | 0.010 max | 0.010 max | 0.3 / 0.5 | Bal | 0.50 | 0.50 |
| Material | Condition | Ultimate Tensile (min) | Yield Strength (Min) | Elongation in 4D % (min) | Hardness | ||
| Mpa | Ksi | Mpa | Ksi | ||||
| Alloy Maraging C250 | After Maraging heat treatment 900°F | 1758 | 255 | 1724 | 250 | 6 | ≥ 48 HRC |
Carey Alloys export products to countries like UAE, Bahrain, Italy, Indonesia, Malaysia, United States, Mexico, Chine, Brazil, Peru, Nigeria, Kuwait, Jordan, Dubai, Thailand (Bangkok), Venezuela, Iran, Germany, UK, Canada, Russia, Turkey, Australia, New Zealand, Sri Lanka, Vietnam, South Africa, Kazakhstan & Saudi Arabia.
HASTELLOY, HAYNES and C-22 are registered trade names of Haynes International, Inc., MONEL & INCONEL are registered trade names of INCO family of companies., NITRONIC is a registered trade name of Armco Inc., CARPENTER & 20Cb-3 are registered trade names of Carpenter Technology Corporation., FERRALIUM is a registered trade name of Langley Alloys, LTD.