Stainles Steel 317L Flanges

Stainless steel flanges from 15NB (1/2”) to 600NB (24”) in Weld neck. Slip-on, Blind, Lap joint, Bossed, Socket Weld and Threaded according to the following standards are available.

As an acclaimed undertaking of the business, Carey Alloys Metal is included in offering an unfathomable cluster of Stainless Steel 317L Flanges as a maker, exporter, stockiest and supplier to our household and worldwide customers. Stainless Steel 317L is the low carbon rendition of 310. It doesn't require post-weld toughening as is widely utilized as a part of substantial gage segments (over around 6mm). Stainless Steel Grade 304H with its higher carbon content discovers application at elevated temperatures.

Regarding diverse evaluations, we offer these Flanges in various sorts, for example, SS Slip On Flanges, SS Blind Flanges, SS Weld Neck Flanges, SS Socket Weld Flanges, SS Spectacle Blind Flanges, SS Screwed/Threaded Flanges, SS Reducing Flanges, and SS Ring Type Joint Flanges (RTJ). In the interim, our costs of such spines are set remembering customers prerequisite.

317L is a molybdenum bearing, low carbon content "L" grade austenitic stainless steel that provides improved corrosion resistance over 304L and 316L stainless steels. The low carbon provides resistance to sensitization during welding and other thermal processes. 317L is non-magnetic in the annealed condition but may become slightly magnetic as a result of welding. 317L has excellent corrosion resistance in a wide range of chemicals, especially in acidic chloride environments such as those encountered in pulp and paper mills. Increased levels of chromium, nickel and molybdenum compared to 316L stainless steel improve resistance to chloride pitting and general corrosion.

317L has excellent corrosion resistance in a wide range of chemicals, especially in acidic chloride environments such as those encountered in pulp and paper mills. Increased levels of chromium, nickel and molybdenum compared to 316L stainless steel improve resistance to chloride pitting and general corrosion. Resistance increases with molybdenum alloy content. 317L is resistant to sulfuric acid concentrations up to 5 percent at temperatures as high as 120°F (49°C).

Applications

  • Flue-gas desulfurization systems
  • Chemical process vessels
  • Petrochemical
  • Pulp and Paper
  • Condensers in power generation

Chemical Composition

SS
317
317L
Ni
11 - 14
11 - 15
N
-
-
Cr
18 – 20
18 - 20
C
0.08 max
0.035 max
Si
1 max
1 max
Mn
2 max
2 max
P
0.040 max
0.040 max
S
0.030 max
0.03 max
Mo
3.00 - 4.00
3 – 4

Mechanical Properties

Density
8.0 g/cm3
Melting Point
1454 °C (2650 °F)
Tensile Strength
Psi – 75000 , MPa – 515
Yield Strength (0.2%Offset)
Psi – 30000 , MPa – 205
Elongation
35 %

Physical Properties

Specific Heat (0-100°C)
Thermal Conductivity
Thermal Expansion
Modulus Elasticity
Electrical Resistivity
Density
500
14.6
16.5
193
7.4
7.99
J.kg-1.°K-1
W.m -1.°K-1
mm/m/°C
GPa
μohm/cm
g/cm3

Carey Alloys exports their products to countries like UAE, Bahrain, Italy, Indonesia, Malaysia, United States, Mexico, Chine, Brazil, Peru, Nigeria, Kuwait, Jordan, Dubai, Thailand (Bangkok), Venezuela, Iran, Germany, UK, Canada, Russia, Turkey, Australia, New Zealand, Sri Lanka, Vietnam, South Africa, Kazakhstan & Saudi Arabia.